research/TCS/2012-09-10/readme

   1 2012-09-10
   2
   3 Arrive 09:40
   4
   5 The interface program left running on 2012-09-07 had crashed at 08:39 on 2012-09-08
   6 This was due to an error in the "process_digits.py" script, which failed to recognise a '0', and caused the program to hang.
   7 I had intended the script to retry if it failed to get a digit, but forgot to remove older code that paused the program and showed the digit to the user.
   8 I have now removed the older section of code. Hopefully if the problem occurs again, the "process_digits.py" script will fail.
   9 "get_pressure.sh" should then take a new photo and try again.
  10
  11 Prepared plots of gun focusing done on 2012-09-07 for Sergey.
  12
  13 File names (under each directory in focus, deflection, accel, venault)
  14 i-v_curves.png - Show all the I-V curves taken varying that electrode
  15 tcs.png - Show the TCS (derivative) of the I-V curves
  16 i-v_max.png - Show maximum I for each electrode setting, and V at which it occurs
  17 tcs_max.png - Show maximum TCS for each electrode setting
  18 tcs_max_position.png - Show position of maximum TCS for each electrode setting
  19
  20 In some cases, also plotted the closest to optimum curves, since there are quite a lot.
  21
  22 Also plot comparison between curves at 11am and 4pm - NOTE: NOT AT OPTIMUM POTENTIALS
  23
  24 And comparison between first curve at optimum potentials on 2012-09-07 and last curve taken before crash on 2012-09-08
  25 "compare_2012-09-07_vs_2012-09-08.png" saved in folder "2012-09-07", symlink in this folder
  26
  27 Noted significant difference, not just in maximum value, but in shape of curve...
  28 Compare TCS as well.
  29
  30 Talked to Sergey
  31  - Parameters aren't necessarily optimum (I know this), best way to optimise is with a cyclical adjustment (I did one cycle only)
  32  - Not much I can do to optimise further, due to time dependence of curves, and long time taken to do a single cycle
  33
  34 Plan:
  35
  36 - Take control measurements of current sample
  37 - Evaporate Au at e-8 mbar for 30min
  38 - Take more measurements, compare
  39 - TURN OFF FILAMENT, turn off turbopump, fill chamber with He gas
  40 - Prepare Black Au (on top of shiny Au) at e-2 mbar for 30min
  41 - Pump down chamber to e-6 mbar
  42 - Take measurements of Black Au
  43 - Compare Black to Shiny Au
  44
  45
  46 Control Measurements
  47 Curves do not resemble curves from 2012-09-07 - slope is far from constant in plateau
  48 - Electrode potentials (Va, Vf, Vd) have changed slightly!
  49 - Reset to optimum values, try again
  50 Va = 126.7V (from 128.8)
  51 Vd = 2.50V (from 2.48)
  52 Vf = -5.50V (from -5.48)
  53 Vv = 23.2V (unchanged)
  54
  55 Shape still looks wierd; extra maxima/minima in derivative.
  56
  57 Manually adjust.
  58 Try:
  59 Va - 126.8V
  60 Vd = 2.69V
  61 Vf = -6.00V
  62 Vv = 23.2V
  63
  64 Still looks wrong, as good as I am going to get.
  65 I hate this experiment.
  66
  67 Record pressure whilst evaporating.
  68
  69