research/TCS/2012-09-13/readme

   1 Arrive 09:50
   2
   3 Au on Si:
   4  - Compare sweeps this morning and last night
   5    - System only did 4 sweeps and stopped, because I forgot to replace "for i in range(0, 4)" with "while true"
   6      - Can still take sweeps this morning, but don't have the full slowly changing set
   7           - FIRST: Fixed dodgy connection on ADC/DAC box. The initial energy appears more stable. DAC = 4000 corresponds to 16.98V.
   8           - Previously DAC = 4000 corresponds to 15-16V, varied if I moved the cable. Now it is stable.
   9
  10    - Current this morning ~1/3 of current yesterday
  11    - Chamber and gun values from 2012-09-12 (yesterday) at 18:28
  12
  13 # Chamber Pressure = 8.55e-08
  14 # Venault Voltage = 10.55
  15 # Accelerating Voltage = 185.3
  16 # Focus Voltage = -20.7
  17 # Deflection Voltage = 6.76
  18 # Initial Voltage = sweep
  19 # Heating Current = 1.135
  20 # Heating Voltage (across filament) = 1.165
  21 # Heating Voltage (across power supply) = 1.52
  22
  23   - Electrode values from 2012-09-13 (today) at 10:06
  24
  25 # Chamber Pressure = 6.45e-08                   ( - 2.10e-8 )
  26 # Venault Voltage = 10.58                       ( + 0.03 )
  27 # Accelerating Voltage = 185.3                  ( same )
  28 # Focus Voltage = -20.7                         ( same )
  29 # Deflection Voltage = 6.76                     ( same )
  30 # Initial Voltage = sweep
  31 # Heating Current = 1.135                       ( same )
  32 # Heating Voltage (across filament) = 1.155     ( - 0.010 )
  33 # Heating Voltage (across power supply) = 1.498 ( - 0.03 )
  34
  35   - Very little change (except in chamber pressure)
  36
  37   - Comparison of plots; generate by running "compare.plt"
  38     - Max current decreases over time. Decrease is significant in 2012-09-12 plots, small in 2012-09-13 plots.
  39         - 2012-09-13 plots ~1/3 max level
  40     - Level of increase moved slightly to left in 2012-09-13 plots.
  41         - This is probably because the ground levels of DAC and power supply are closer now.
  42     - Width of increase appears the same
  43     - Plateau is flatter in 2012-09-13 plots
  44
  45 - Take a few more sweeps, then prepare Black Au.
  46   - Hopefully will actually get it done this time.
  47
  48   - Had to go to tutorial at 11:00, then had lunch... then QFT Tutorial... didn't get back until 14:08
  49     - Sweeps all appear similar, slight downward drift in maximum current
  50       - I really hope the filament doesn't die.
  51
  52   - Prepare Black Au !
  53      - pressure monitored in 1408.pressure.dat every 5s
  54         - Evaporate at 3.1A - entire ball melts after 18mins
  55
  56   - Decrease pressure; turn turbo pump back on. Pressure still in 1408.pressure.dat (pump turned on after t = ~2580s)
  57   - Turn on filament (2980s) monitor sample current with max initial energy, wait for stabilise, then take TCS
  58     - Or don't wait
  59       - Note shift in work function from ~500 to ~800 counts
  60
  61   - Plan:
  62      - Take TCS of Black Au
  63      - Evaporate shiny Au on top
  64      - See if TCS returns to original form
  65      - Then vent chamber, turn off everything for electricians on Friday