research/TCS/2012-10-04/160152.dat

   1 # File opened at 2012-10-04 16:01:52.794475
   2 # aquire[DAC_Settle] = 0.0
   3 # aquire[open_files] = [<open file '2012-10-04/160152.dat', mode 'w' at 0x187cc00>]
   4 # aquire[DAC_Sweep] = 0.0 + 100.0*int(step)
   5 # aquire[ADC_Averages] = 200
   6 # aquire[start_date] = 2012-10-04
   7 # Parameters:
   8 # Chamber Pressure = 2.34e-08
   9 # Deflection Voltage = -2.06
  10 # Title = Au (230min) on Si
  11 # Comment = Focused (?) now
  12 # 602 Scale = 1e-7 x 0.1
  13 # Venault Voltage = 10.48
  14 # Accelerating Voltage = 262
  15 # Focus Voltage = 45
  16 # Initial Voltage = sweep
  17 # Heating Current = 1.149
  18 # Heating Voltage (across filament) = 1.179
  19 # Heating Voltage (across power supply) = 1.578
  20 # 602 Zero = 0.00
  21 # 602 0.1 Battery = 7.98
  22 # 602 0.03 Battery = 8.35
  23 # 602 0.01 Battery = 8.12
  24 # 602 0.003 Battery = 8.12
  25 # 602 0.001 Battery = 8.22
  26 # Sample = Au (30min 4.8A + 60+20min 4.6A + 20+30+70min 4.0A e-8mbar)
  27 # Sample Angle = 142
  28 # ADC Regulator = 3.32
  29 # Data = time DAC ADC5 ADC5_sigma
  30 # Parameters last checked = 2012-10-04 16:00:12.388593
  31
  32 # Experiment 2012-10-04 16:01:53.332086
  33 # Polling for Nones.
  34
  35 # Data:
  36 # time  DAC     ADC5
  37 2.528175354     0       0.0     0.0
  38 3.16455793381   100     0.0     0.0
  39 3.80458545685   200     0.0     0.0
  40 4.44155693054   300     0.0     0.0
  41 5.08053636551   400     0.0     0.0
  42 5.72053527832   500     0.0     0.0
  43 6.36300444603   600     0.0     0.0
  44 7.008507967     700     0.0     0.0
  45 7.64453887939   800     0.0     0.0
  46 8.28454113007   900     0.0     0.0
  47 8.92452740669   1000    0.0     0.0
  48 9.56702637672   1100    0.0     0.0
  49 10.2125458717   1200    0.0     0.0
  50 10.8550169468   1300    0.0     0.0
  51 11.5030097961   1400    0.0     0.0
  52 12.1485199928   1500    0.0     0.0
  53 12.8505530357   1600    3.42    2.18
  54 13.6245274544   1700    74.23   6.80
  55 14.4025158882   1800    158.2   9.45
  56 15.1885244846   1900    252.9   8.94
  57 15.9925243855   2000    350.98  6.13
  58 16.7990274429   2100    401.51  5.5
  59 17.6075406075   2200    439.62  4.64
  60 18.4145383835   2300    470.75  4.52
  61 19.2225439548   2400    494.58  4.6
  62 20.0390334129   2500    513.51  3.45
  63 20.8570249081   2600    523.23  3.5
  64 21.679017067    2700    528.47  2.86
  65 22.5075125694   2800    531.37  2.82
  66 23.3345365524   2900    530.53  2.70
  67 24.1625418663   3000    527.22  2.71
  68 24.9925179482   3100    522.85  2.34
  69 25.8185424805   3200    514.64  2.29
  70 26.6285438538   3300    506.77  2.41
  71 27.4370346069   3400    499.93  2.65
  72 28.2495760918   3500    497.57  2.61
  73 29.0530414581   3600    498.1   2.83
  74 29.8635263443   3700    499.47  2.70
  75 30.6725449562   3800    500.85  2.68
  76 31.4805364609   3900    502.88  2.64
  77 32.2885255814   4000    504.57  2.51
  78 # File closed at 2012-10-04 16:02:26.244598