research/TCS/2012-10-04/focus/focus/Vf=0.00/140230.dat

   1 # File opened at 2012-10-04 14:02:30.727266
   2 # aquire[DAC_Settle] = 0.0
   3 # aquire[open_files] = [<open file '2012-10-04/140230.dat', mode 'w' at 0x2c82c00>]
   4 # aquire[DAC_Sweep] = 0.0 + 100.0*int(step)
   5 # aquire[ADC_Averages] = 200
   6 # aquire[start_date] = 2012-10-04
   7 # Parameters:
   8 # Chamber Pressure = 2.27e-08
   9 # Deflection Voltage = -0.799
  10 # Title = Focus on Au (230min) on Si
  11 # Comment = Adjust focus electrodes
  12 # 602 Scale = 1e-6 x 0.1
  13 # Venault Voltage = 10.34
  14 # Accelerating Voltage = 264
  15 # Focus Voltage = 0.00
  16 # Initial Voltage = sweep
  17 # Heating Current = 1.149
  18 # Heating Voltage (across filament) = 1.179
  19 # Heating Voltage (across power supply) = 1.578
  20 # 602 Zero = 0.00
  21 # 602 0.1 Battery = 7.98
  22 # 602 0.03 Battery = 8.35
  23 # 602 0.01 Battery = 8.12
  24 # 602 0.003 Battery = 8.12
  25 # 602 0.001 Battery = 8.22
  26 # Sample = Au (30min 4.8A + 60+20min 4.6A + 20+30+70min 4.0A e-8mbar)
  27 # Sample Angle = 142
  28 # ADC Regulator = 3.32
  29 # Data = time DAC ADC5 ADC5_sigma
  30 # Parameters last checked = 2012-10-04 14:02:30.720897
  31
  32 # Experiment 2012-10-04 14:02:31.263011
  33 # Polling for Nones.
  34
  35 # Data:
  36 # time  DAC     ADC5
  37 2.55524110794   0       0.0     0.0
  38 3.1960940361    100     0.0     0.0
  39 3.82960748672   200     0.0     0.0
  40 4.47161436081   300     0.0     0.0
  41 5.10570693016   400     0.0     0.0
  42 5.74565410614   500     0.0     0.0
  43 6.3856048584    600     0.0     0.0
  44 7.02161312103   700     0.0     0.0
  45 7.66263246536   800     0.0     0.0
  46 8.29769945145   900     0.0     0.0
  47 8.94358706474   1000    0.0     0.0
  48 9.59010052681   1100    0.0     0.0
  49 10.2395939827   1200    0.0     0.0
  50 10.8880748749   1300    0.0     0.0
  51 11.5336151123   1400    0.0     0.0
  52 12.1716349125   1500    0.0     0.0
  53 12.8216004372   1600    0.0     0.0
  54 13.4720799923   1700    0.0     0.0
  55 14.1855964661   1800    10.51   1.98
  56 14.9635939598   1900    31.60   3.27
  57 15.742105484    2000    58.3    3.87
  58 16.5196428299   2100    85.55   3.27
  59 17.3155839443   2200    106.87  2.76
  60 18.1041073799   2300    124.19  2.61
  61 18.8995909691   2400    140.2   2.70
  62 19.6881198883   2500    155.11  2.97
  63 20.4755768776   2600    168.5   3.8
  64 21.2635874748   2700    179.31  3.4
  65 22.0520935059   2800    191.43  3.31
  66 22.84760499     2900    204.55  3.67
  67 23.6356034279   3000    218.59  4.3
  68 24.4236073494   3100    232.45  3.94
  69 25.2116556168   3200    246.6   3.67
  70 26.0135974884   3300    257.2   3.20
  71 26.8355975151   3400    265.70  3.16
  72 27.6615920067   3500    272.38  3.4
  73 28.4751684666   3600    278.66  3.9
  74 29.2835893631   3700    284.43  3.1
  75 30.1056559086   3800    289.95  2.75
  76 30.9215950966   3900    294.59  2.63
  77 31.7401123047   4000    298.68  2.49