research/TCS/preliminary/29-06-2012/13:05.dat

   1 # Trying to optimise lens setup
   2
   3
   4 # Va = 200 V
   5
   6 # If = 1.22 A
   7 # Vd = 0.00 V
   8 # Vv = 17.38 V
   9
  10 # Start at 13:11
  11
  12 # Vf = -50.7
  13 # Vi    Ie      Is      Vf
  14 0.00    6.4     0.0000  -50.7
  15 1.01    6.4     0.0003  -50.7
  16 2.00    6.4     0.0007  -50.7
  17 3.00    6.4     0.0020  -50.7
  18 3.52    6.4     0.0022  -50.7
  19 4.02    6.5     0.0030  -50.7
  20 4.54    6.4     0.0038  -50.7
  21 5.01    6.5     0.0040  -50.7
  22 6.00    6.5     0.0047  -50.7
  23 7.00    6.5     0.0057  -50.7
  24 7.98    6.5     0.0060  -50.7
  25 9.04    6.5     0.0062  -50.7
  26 10.05   6.6     0.0075  -50.7
  27 11.02   6.6     0.0080  -50.7
  28 12.00   6.6     0.0087  -50.7
  29 13.03   6.6     0.0098  -50.7
  30 14.01   6.6     0.0104  -50.7
  31 15.04   6.7     0.0122  -50.7
  32 16.00   6.7     0.0128  -50.7
  33 17.20   6.7     0.0130  -50.7
  34
  35 # Vf = -40.0
  36 # Vi    Ie      Is      Vf
  37 0.00    6.2     0.0000  -40.0
  38 1.00    6.3     0.0002  -40.0
  39 2.00    6.3     0.0004  -40.0
  40 2.50    6.3     0.0018  -40.0
  41 3.00    6.3     0.0033  -40.0
  42 3.51    6.4     0.0041  -40.0
  43 4.02    6.3     0.0050  -40.0
  44 4.50    6.4     0.0060  -40.0
  45 5.01    6.4     0.0063  -40.0
  46 6.01    6.4     0.0082  -40.0
  47 7.01    6.4     0.0100  -40.0
  48 8.00    6.4     0.0112  -40.0
  49 9.02    6.5     0.0120  -40.0
  50 10.02   6.5     0.0128  -40.0
  51 11.05   6.5     0.0140  -40.0
  52 11.99   6.5     0.0150  -40.0
  53 13.00   6.6     0.0164  -40.0
  54 14.00   6.6     0.0182  -40.0
  55 15.00   6.6     0.0202  -40.0
  56 16.00   6.6     0.0222  -40.0
  57 17.20   6.7     0.0230  -40.0
  58
  59 # Vf = -30.0
  60 # Vi    Ie      Is      Vf
  61 0.00    6.2     0.0000  -30.0
  62 1.01    6.2     0.0002  -30.0
  63 2.02    6.2     0.0010  -30.0
  64 2.50    6.2     0.0023  -30.0
  65 3.00    6.2     0.0042  -30.0
  66 3.49    6.3     0.0062  -30.0
  67 4.01    6.3     0.0080  -30.0
  68 4.49    6.3     0.0092  -30.0
  69 5.01    6.3     0.0105  -30.0
  70 6.00    6.3     0.0132  -30.0
  71 7.03    6.3     0.0158  -30.0
  72 8.03    6.3     0.0178  -30.0
  73 9.01    6.4     0.0190  -30.0
  74 10.03   6.4     0.0202  -30.0
  75 11.00   6.4     0.0221  -30.0
  76 11.99   6.4     0.0242  -30.0
  77 13.02   6.5     0.0270  -30.0
  78 14.00   6.5     0.0298  -30.0
  79 15.03   6.5     0.0330  -30.0
  80 16.00   6.5     0.0358  -30.0
  81 17.20   6.5     0.0375  -30.0
  82
  83 # Vf = -20.0
  84 # Vi    Ie      Is      Vf
  85 0.00    6.1     0.0000  -20.0
  86 1.02    6.1     0.0001  -20.0
  87 2.00    6.2     0.0010  -20.0
  88 2.50    6.2     0.0035  -20.0
  89 3.03    6.2     0.0062  -20.0
  90 3.50    6.2     0.0088  -20.0
  91 4.00    6.2     0.0118  -20.0
  92 4.50    6.2     0.0138  -20.0
  93 5.00    6.2     0.0153  -20.0
  94 6.00    6.2     0.0198  -20.0
  95 7.00    6.3     0.0238  -20.0
  96 8.01    6.3     0.0262  -20.0
  97 9.01    6.3     0.0290  -20.0
  98 10.00   6.4     0.0318  -20.0
  99 11.00   6.3     0.0340  -20.0
 100 12.04   6.4     0.0368  -20.0
 101 13.00   6.4     0.0400  -20.0
 102 14.00   6.4     0.0440  -20.0
 103 15.08   6.4     0.0492  -20.0
 104 16.00   6.4     0.0537  -20.0
 105 17.20   6.5     0.0562  -20.0
 106
 107 # Vf = -10.0
 108 # Vi    Ie      Is      Vf
 109 0.00    6.1     0.0000  -10.0
 110 1.02    6.1     0.0000  -10.0
 111 2.00    6.1     0.0000  -10.0
 112 2.50    6.2     0.0002  -10.0
 113 3.00    6.1     0.0003  -10.0
 114 3.50    6.2     0.0008  -10.0
 115 4.02    6.2     0.0012  -10.0
 116 4.50    6.2     0.0028  -10.0
 117 5.02    6.2     0.0050  -10.0
 118 6.04    6.2     0.0074  -10.0
 119 7.00    6.2     0.0091  -10.0
 120 8.00    6.2     0.0118  -10.0
 121 9.02    6.3     0.0138  -10.0
 122 10.06   6.3     0.0160  -10.0
 123 11.01   6.3     0.0183  -10.0
 124 11.99   6.3     0.0200  -10.0
 125 13.01   6.4     0.0210  -10.0
 126 14.02   6.4     0.0221  -10.0
 127 15.05   6.4     0.0236  -10.0
 128 16.04   6.4     0.0242  -10.0
 129 17.21   6.4     0.0258  -10.0
 130
 131 # Vf = 0.0
 132 # Vi    Ie      Is      Vf
 133 0.00    6.0     0.0000  0.0
 134 1.01    6.0     0.0001  0.0
 135 2.00    6.1     0.0001  0.0
 136 2.50    6.1     0.0001  0.0
 137 3.00    6.1     0.0001  0.0
 138 3.99    6.1     0.0001  0.0
 139 4.58    6.1     0.0008  0.0
 140 5.03    6.1     0.0018  0.0
 141 6.01    6.1     0.0038  0.0
 142 7.01    6.2     0.0050  0.0
 143 8.00    6.2     0.0062  0.0
 144 9.04    6.2     0.0080  0.0
 145 10.01   6.2     0.0098  0.0
 146 11.02   6.2     0.0122  0.0
 147 12.02   6.3     0.0143  0.0
 148 13.01   6.3     0.0160  0.0
 149 14.01   6.3     0.0162  0.0
 150 15.01   6.3     0.0170  0.0
 151 16.00   6.3     0.0178  0.0
 152 17.21   6.4     0.0182  0.0
 153
 154 # Stop 14:05
 155
 156 # Conclusions:
 157 # From plot, it seems that Vf = -20.0 = 0.1 Va is optimal
 158 # Will adjust slightly.
 159
 160 # The dependence of Ie (emission current) on Vi suggests there is current flowing through electrodes.
 161 # Suspect the Venault (Vv), as it is significantly high and close to the electrode.
 162 # Possibly also Va
 163 # Hopefully, it is the ratio of Vf/Va that matters, so I do not need to repeat all this if I change Va and/or Vv (!)