research/ellipsometry/WVASE32/Mat/Semicond/Znse_2.mat

   1 ZnSe, from sample #5\r
   2 nm\r
   3 NK\r
   4 500     2.8092  0.050541\r
   5 510     2.7896  0.046322\r
   6 520     2.7688  0.041765\r
   7 530     2.7476  0.038401\r
   8 540     2.7289  0.034612\r
   9 550     2.7131  0.030256\r
  10 560     2.697   0.025496\r
  11 570     2.6853  0.021768\r
  12 580     2.6731  0.017815\r
  13 590     2.6615  0.013882\r
  14 600     2.6518  0.010744\r
  15 610     2.6426  0.0078515\r
  16 620     2.6338  0.0051923\r
  17 630     2.6255  0.0032151\r
  18 640     2.6182  0.0014969\r
  19 650     2.6111  0.0002147\r
  20 660     2.6076  0\r
  21 670     2.5999  0\r
  22 680     2.5952  0\r
  23 690     2.5905  0\r
  24 700     2.5869  0\r
  25 710     2.5826  0\r
  26 720     2.5788  0\r
  27 730     2.5747  0\r
  28 740     2.5712  0\r
  29 750     2.5678  0\r
  30 760     2.564   0\r
  31 770     2.5606  0\r
  32 780     2.5567  0\r
  33 790     2.5527  0\r
  34 800     2.55    0\r
  35 810     2.5464  0\r
  36 820     2.542   0\r
  37 830     2.5402  0\r
  38 840     2.5362  0\r
  39 850     2.5344  0\r
  40 860     2.5384  0.0036127\r
  41 870     2.528   0\r
  42 880     2.5253  0\r
  43 890     2.5241  0.00027255\r
  44 900     2.5222  0.00040218\r
  45 910     2.5198  0.00040317\r
  46 920     2.518   0.00035322\r
  47 930     2.5155  0.00019728\r
  48 940     2.5136  6.4507e-005\r
  49 950     2.5117  5.8511e-005\r
  50 960     2.5102  0.00011607\r
  51 970     2.5081  0\r
  52 980     2.5065  0\r
  53 990     2.5044  0\r
  54 1000    2.5036  0\r
  55 1010    2.5018  0\r
  56 1020    2.5009  0\r
  57 1030    2.499   0.00017577\r
  58 1040    2.4977  0\r
  59 1050    2.4965  0\r
  60 1060    2.4957  0\r
  61 1070    2.4943  0\r
  62 1080    2.493   0\r
  63 1090    2.4918  0\r
  64 1100    2.4914  0\r
  65 1110    2.4899  0\r
  66 1120    2.489   0\r
  67 1130    2.4879  0\r
  68 1140    2.4875  0\r
  69 1150    2.4867  0.00043305\r
  70 1160    2.4855  0.00013496\r
  71 1170    2.485   6.5382e-005\r
  72 1180    2.4843  4.1022e-005\r
  73 1190    2.4837  0\r
  74 1200    2.483   0.00022221\r
  75 1210    2.4824  0.00065129\r
  76 1220    2.4807  0.0002759\r
  77 1230    2.4818  0.0003911\r
  78 1240    2.4864  0\r
  79 1250    2.4814  0.00027767\r
  80 1260    2.4737  0.00018421\r
  81 1270    2.4779  0.00020679\r
  82 1280    2.4764  0\r
  83 1290    2.474   7.215e-005\r
  84 1300    2.4768  0.0010915\r
  85 1310    2.4755  0\r
  86 1320    2.4758  0\r
  87 1330    2.4756  0\r
  88 1340    2.4766  0\r
  89 1350    2.4767  0.00046359\r
  90 1360    2.4764  0.0011609\r
  91 1370    2.4757  0\r
  92 1380    2.4757  0.0026789\r
  93 1390    2.4727  0.0038377\r
  94 1400    2.47    0.00091898\r
  95 1410    2.4739  8.7353e-005\r
  96 1420    2.4721  0\r
  97 1430    2.4747  0.0010406\r
  98 1440    2.4714  0\r
  99 1450    2.4732  6.0741e-005\r
 100 1460    2.4743  0.00050103\r
 101 1470    2.4742  0\r
 102 1480    2.473   0\r
 103 1490    2.4741  0\r
 104 1500    2.4749  0.00055914\r
 105 1510    2.4731  0\r
 106 1520    2.4744  0\r
 107 1530    2.4743  0\r
 108 1540    2.4733  0.00027333\r
 109 1550    2.473   0\r
 110 1560    2.4694  0.00051404\r
 111 1570    2.4726  0.0060484\r
 112 1580    2.4704  0\r
 113 1590    2.4693  0.00096391\r
 114 1600    2.469   0.0022612\r
 115 1610    2.4694  0.0010087\r
 116 1620    2.4664  0.0019392\r
 117 1630    2.4701  0\r
 118 1640    2.475   0.002113\r
 119 1650    2.4677  0\r
 120 1660    2.4664  0.0012358\r
 121 1670    2.471   0.0037198\r
 122 1680    2.4739  0.0049986\r
 123 1690    2.4368  0.021326\r
 124 1700    2.4427  0