+GaAs: Si 5.5x1018/cm3 at RT, measured by H. Yao. \r
+EV\r
+E1E2\r
+4.9994 -6.03 20.544\r
+4.94951 -5.819 21.926\r
+4.89866 -4.834 23.408\r
+4.84885 -3.207 24.131\r
+4.79819 -1.492 24.549\r
+4.74857 0.052 24.61\r
+4.69819 1.638 24.413\r
+4.64886 3.165 24.094\r
+4.59886 4.532 23.591\r
+4.54825 5.897 22.918\r
+4.49874 7.039 22.123\r
+4.4487 8.333 21.056\r
+4.3982 9.092 19.699\r
+4.34883 9.571 18.47\r
+4.29907 9.723 17.354\r
+4.24898 9.581 16.368\r
+4.19862 9.465 15.669\r
+4.14805 9.336 15.068\r
+4.09868 9.177 14.586\r
+4.04916 8.892 14.186\r
+3.99952 8.777 13.972\r
+3.94983 8.61 13.782\r
+3.90013 8.449 13.653\r
+3.85047 8.243 13.55\r
+3.80089 8.174 13.582\r
+3.75144 8.1 13.626\r
+3.70105 7.98 13.64\r
+3.65092 7.985 13.833\r
+3.60108 7.905 13.951\r
+3.55157 7.916 14.217\r
+3.50142 8.03 14.501\r
+3.4517 8.022 14.893\r
+3.40151 8.273 15.346\r
+3.35186 8.425 15.838\r
+3.30187 8.912 16.528\r
+3.25164 9.464 17.294\r
+3.20127 10.28 18.073\r
+3.15163 11.62 18.88\r
+3.10196 13.547 19.147\r
+3.05232 15.797 18.486\r
+3.00206 17.05 17.704\r
+2.95203 18.219 17.486\r
+2.90227 20.512 16.641\r
+2.8522 22.621 14.099\r
+2.80192 22.973 11.148\r
+2.75217 22.34 8.99\r
+2.70238 21.378 7.476\r
+2.65266 20.61 6.291\r
+2.60254 19.802 5.525\r
+2.55271 19.13 4.907\r
+2.50273 18.63 4.311\r
+2.45272 18.101 3.876\r
+2.40281 17.635 3.539\r
+2.35266 17.213 3.24\r
+2.30285 16.796 3.077\r
+2.25305 16.44 2.854\r
+2.20301 16.168 2.594\r
+2.15289 15.881 2.407\r
+2.10287 15.635 2.244\r
+2.05273 15.388 2.203\r
+2.00267 15.211 1.952\r
+1.95252 15.013 1.766\r
+1.90249 14.794 1.704\r
+1.85246 14.608 1.582\r
+1.80237 14.493 1.351\r
+1.75244 14.353 1.318\r
+1.70239 14.277 1.043\r
+1.65247 14.195 0.804\r
+1.6025 13.996 0.538\r
+1.55253 13.819 0.273\r
+1.50249 13.325 0.165\r