research/TCS/2012-10-03/Au (100min) on Si/143841.dat

   1 # File opened at 2012-10-03 14:38:41.975795
   2 # aquire[DAC_Settle] = 0.0
   3 # aquire[open_files] = [<open file '2012-10-03/143841.dat', mode 'w' at 0x24b6c00>]
   4 # aquire[DAC_Sweep] = 0.0 + 10.0*int(step)
   5 # aquire[ADC_Averages] = 200
   6 # aquire[start_date] = 2012-10-03
   7 # Parameters:
   8 # Chamber Pressure = 1.49e-08
   9 # Deflection Voltage = -0.608
  10 # Title = Au(70min) on Si
  11 # Comment = Au layer still not visible (current too low?)
  12 # 602 Scale = 1e-6 x 0.1
  13 # Venault Voltage = 10.35
  14 # Accelerating Voltage = 264
  15 # Focus Voltage = 8.17
  16 # Initial Voltage = sweep
  17 # Heating Current = 1.149
  18 # Heating Voltage (across filament) = 1.181
  19 # Heating Voltage (across power supply) = 1.561
  20 # 602 Zero = 0.00
  21 # 602 0.1 Battery = 8.05
  22 # 602 0.03 Battery = 8.40
  23 # 602 0.01 Battery = 8.20
  24 # 602 0.003 Battery = 8.18
  25 # 602 0.001 Battery = 8.22
  26 # Sample = Au (30min + 70min 4.0A e-8mbar) on Si
  27 # Sample Angle = 142
  28 # ADC Regulator = 3.32
  29 # Data = time DAC ADC5 ADC5_sigma
  30 # Parameters last checked = 2012-10-03 13:52:44.536577
  31
  32 # Experiment 2012-10-03 14:38:42.484607
  33 # Polling for Nones.
  34
  35 # Data:
  36 # time  DAC     ADC5
  37 2.52715206146   0       0.0     0.0
  38 3.16204309464   10      0.0     0.0
  39 3.80254459381   20      0.0     0.0
  40 4.43669700623   30      0.0     0.0
  41 5.06419849396   40      0.0     0.0
  42 # Recieved KILL signal.
  43 # Reason: Stop for evaporation
  44 # File closed at 2012-10-03 14:38:51.288719