research/TCS/2012-10-03/readme

   1 Arrive 11:05am
   2
   3 - Look at results of Au on Si started on 2012-09-27
   4 - Curve has developed the "double peak" in slope !
   5
   6 - Check chamber properties!
   7
   8 - On 2012-09-27
   9
  10 # Chamber Pressure = 0.0
  11 # Deflection Voltage = -0.59
  12 # Venault Voltage = 10.35
  13 # Accelerating Voltage = 264
  14 # Focus Voltage = 8.17
  15 # Heating Current = 1.149
  16 # Heating Voltage (across filament) = 1.176
  17 # Heating Voltage (across power supply) = 1.503
  18
  19 - Today (2012-10-03)
  20
  21 # Chamber Pressure = 1.14e-08
  22 # Deflection Voltage = -0.605
  23 # Venault Voltage = 10.34
  24 # Accelerating Voltage = 264
  25 # Focus Voltage = 8.18
  26 # Heating Current = 1.149
  27 # Heating Voltage (across filament) = 1.181
  28 # Heating Voltage (across power supply) = 1.561
  29
  30 - Little change in gun properties => Sample has changed over time
  31
  32 - Make movie showing change in curves
  33   - That was nice, but doesn't really tell me anything I didn't know
  34     - Other than that the change was consistently in the same direction, and gradual
  35
  36 - Now! The preparation of more Au!!!
  37
  38 - Curves appear very similar to the curves on 2012-09-27... before they changed
  39   - Hmmmmmm
  40   - I don't have a week to see if the same thing happens
  41   - Layer of Au still not visible
  42
  43 - Prepare more Au at higher current
  44  - Leave TCS running overnight
  45